Virgin Molding – RB

HaloPolymer PTFE grade RB is a granular powder product designed for general purpose compression molding. This fully fluorinated resin has excellent chemical stability, electrical and mechanical properties.

Product overview:

This virgin granular PTFE is suited for compression molding. This material can be used for production of articles for chemical, mechanical and low-friction applications.

Typical applications:

Can be used as a raw material for production of pre-sintered and fine cut grades. Grade RB can also be used fot general purposes: molded sheets, small parts, etc.

Availability:

30 kg cardbox with 2×15 kg polyethylene inserts.

TYPICAL PROPERTIES OF PTFE GRADE RB

Properties

Test Method

Units

Typical Value, RB

ASTM Type/Grade

ASTM D4894

I

Bulk density

ASTM D4894

g/l

550

Average particle size (d50)

Internal, Laser Scatt.

µm

250

Mould shrinkage

ASTM D4894

%

2,2

Std. specific gravity (SSG)

ASTM D4894

g/cm3

2,15

Melting points

DSC

°C (°F)

342 (648) (Initial)
327 (621) (Second)

380 (716)

Sintering temperature

Internal

°C (°F)

Tensile strength

ASTM D4894

MPa (psi)

20 (2900)

Elongation at break

ASTM D4894

%

250

CERTIFICATION

Certificate of conformity FDA 21 CFR 177.1380 & FDA 21 CFR 177.1550

PTFE

Intertek Polychemlab

USA

Certificate of conformity Class VI acc. USP 35 <88>

PTFE

Pacific BioLabs

USA

Declaration of Compliance commission reg. (EU) 10/2011

PTFE

SGS Multilab

EU

PRODUCT DESCRIPTION

HaloPolymer PTFE granular powder RB is a product of suspension polymerization of TFE subjected to grinding. This grade can be used for production of a variety of general purpose articles by compression molding technique.

PROCESSING BASICS

Conventional plastics processing techniques are not suitable for PTFE resin processing due to its high melting temperature and very high melt viscosity.

Grade RB fabrication includes mould pressing of PTFE powder at ambient temperature, preform sintering in several stages with the maximum temperature of 380° C and subsequent controlled cooling. Billets can be further processed into finished articles by machining or cutting.

STORAGE AND HANDLING

Bags with PTFE powder should be stored in a cold dry place. Recommended storage temperature range is 15-20 °C. Bags with powder stored below this range should be kept closed until warmed to room temperature. Optimal temperature range for PTFE compression moulding is 20-25°C. Below this temperature PTFE changes its crystalline structure with volume variation of 1-2%, causing formation of cracks in preforms.

Mechanical manipulations with PTFE powders should be reduced. At the temperature higher than 30°C PTFE tends to form clumps.

PTFE powders attract dust and moisture from ambience and should be processed at clean and dry conditions.

Sintering of PTFE is linked to an emission of toxic gaseous products. Therefore sintering process should be performed in a ventilated area. Air from the processing zone must be evacuated.

PRESSING

The pressing process of PTFE powder requires careful powder de- clumping. Uniform layer-by-layer mold filling is essential to avoid cracks formation in preform. The temperature of PTFE powder should be kept above 19° C.

Mold filled with PTFE powder is pressed into a solid preform with density of 1,80-2,00 kg/l.

Compression ratio parameter indicates volume compaction of powder during the pressing process. It is based on a preform/bulk density ratio. The rate of ram travel is adjusted to allow air to leave preform.

TYPICAL MOLDING PROPERTIES

Properties

RB

Bulk density, g/l

550

Compression ratio

~3,5

Molding pressure, MPa

30-35

MACHINING

PTFE billets are machined in the same way that mild metals are. Sharp steel cutting tools are suitable for the machining process. PTFE billets designed for further skived films production are processed at elevated temperatures.

Back to Polytetrafluoroethylene (PTFE)